Zinc Plated Rod Properties
| Hardness, Brinell | 163 | 163 | ||
| Hardness, Knoop | 184 | 184 | Converted from Brinell hardness. | |
| Hardness, Rockwell B | 84 | 84 | Converted from Brinell hardness. | |
| Hardness, Vickers | 170 | 170 | Converted from Brinell hardness. | |
| Tensile Strength, Ultimate | 540 MPa | 78300 psi | ||
| Tensile Strength, Yield | 415 MPa | 60200 psi | ||
| Elongation at Break | 10 % | 10 % | ||
| Reduction of Area | 35 % | 35 % | ||
| Modulus of Elasticity | 200 GPa | 29000 ksi | Typical for steel | |
| Bulk Modulus | 140 GPa | 20300 ksi | Typical for steel. | |
| Poisson's Ratio | 0.29 | 0.29 | Typical For Steel | |
| Machinability | 160 % | 160 % | Based on 100% machinability for AISI 1212 steel. | |
| Shear Modulus | 80 GPa | 11600 ksi | Typical for steel. | |
Electrical Properties |
||||
|
|
||||
| Electrical Resistivity | 1.74e-005 ohm-cm | 1.74e-005 ohm-cm | Typical steel | |
Thermal Properties |
||||
|
|
||||
| CTE, linear 20°C | 11.5 μm/m-°C | 6.39 μin/in-°F | Typical steel | |
| CTE, linear 250°C | 12.2 μm/m-°C | 6.78 μin/in-°F | Typical for steel ; 0-300°C (68-570°F) | |
| CTE, linear 500°C | 13.9 μm/m-°C | 7.72 μin/in-°F | Typical for steel ; 0-500°C (68-930°F) | |
| CTE, linear 1000°C | 14.7 μm/m-°C | 8.17 μin/in-°F | Typical steel | |
| Specific Heat Capacity | 0.472 J/g-°C | 0.113 BTU/lb-°F | Typical steel | |
| Thermal Conductivity | 51.9 W/m-K | 360 BTU-in/hr-ft2-°F | Typical steel | |