5005 H34 Aluminum Data
This is a non-heat treatable alloy of aluminum with magnesium content. Cold working will strengthen (harden) the alloy and it is very good in both corrosion resistance and weldability.
Note: K-mac does not sell this grade - Data is for reference only.
| Aluminum | Balance |
| Chromium | 0.1 max |
| Copper | 0.2 max |
| Iron | 0.7 max |
| Magnesium | 0.5 - 1.1 |
| Manganese | 0.2 max |
| Remainder Each | 0.05 max |
| Remainder Total | 0.15 max |
| Silicon | 0.4 max |
| Zinc | 0.25 max |
| Density | 0.0975 lb/in3 |
| Hardness, Brinell | 41 |
| Tensile Strength | 23000 psi |
| Tensile Yield Strength | 20000 psi |
| Elongation at Break | 8 % |
| Modulus of Elasticity | 10000 ksi |
| Poisson's Ratio | 0.33 |
| Shear Modulus | 3760 ksi |
| Shear Strength | 14000 psi |
| Electrical Resistivity | 3.32e-006 ohm-cm |
| CTE, linear 68°F | 13.2 μin/in-°F |
| CTE, linear 250°C | 14.2 μin/in-°F |
| Specific Heat Capacity | 0.215 BTU/lb-°F |
| Thermal Conductivity | 1390 BTU-in/hr-ft2-°F |
| Melting Point | 1170 - 1210 °F |