7075 T73511 Aluminum Data
Silicon: 0.40
Iron: 0.50
Copper: 1.2 - 2.0
Manganese: 0.30
Magnesium: 2.1 - 2.9
Chromium: 0.18 - 0.28
Zinc: 5.1 - 6.1
Titanium: 0.20
Aluminum: Remainder
Density | 0.102 lb/in3 |
Hardness, Brinell | 135 |
Tensile Strength, | 73200 psi |
Tensile Strength, Yield | 63100 psi |
Elongation at Break | 13 % |
Modulus of Elasticity | 10400 ksi |
Poisson's Ratio | 0.33 |
Fatigue Strength | 21800 psi |
Fracture Toughness | 18.2 ksi-√in. |
Machinability | 70 % |
Shear Modulus | 3900 ksi |
Shear Strength | 43500 psi |
Electrical Resistivity | 4.3e-006 ohm-cm |
CTE, linear 68°F | 13.1 μin/in-°F |
CTE, linear 250°C | 14 μin/in-°F |
Specific Heat Capacity | 0.229 BTU/lb-°F |
Thermal Conductivity | 1080 BTU-in/hr-ft2-°F |
Melting Point | 890 - 1175 °F |
Annealing Temperature | 775 °F |